1. CG-A361C
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Applications:
Characteristics:
Fluorine Content: 66 percent
Specific gravity: 1.82
Color: permalba
Solubility: low-molecular-weight ketone or ester.
Mooney viscosity: 30（ML1+10@121℃）
2. CG-A401C
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Contents: binary mixture of vinylidene fluoride and hexafluoropropylene.
Moderate Mooney
Processing mode: mold pressing, flow mold pressing.
Characteristics: unique techniques for vulcanizing agent mixing, with good mold unload properties and scorch safety; applicable to O rings or washers.
Fluorine content: 66 percent
Specific gravity: 1.82
Color: permalba
Solubility: ketone, ester.
Mooney viscosity: 42（ML1+10@121℃）
3. CG-F2602AP
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Contents: binary mixture of vinylidene fluoride and hexafluoropropylene; general fluorine mixed glue
Moderate Mooney
Processing mode: mold pressing, flow mold pressing, extrusion molding.
Characteristics unique technique for vulcanizing agent mixing; good mobility, mold unload property and scorch safety; can be used as sealing material of complex shape.
Fluorine content: 66 percent
Specific gravity: 1.82
Color: permalba
Solubility: low-molecular-weight ketone or ester
Mooney viscosity: 38（ML1+10@121℃ ）
4. GC-A45P
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Contents: binary mixture of vinylidene fluoride and hexafluoropropylene, vulcanizing agent included.
Characteristics: high viscous CG A25P, very good hot tear resistance and high curing speed.
Processing mode: extrusion molding, mold pressing, transfer molding.
Vulcanization: bisphenol
Fluorine content: 66 percent
Specific gravity: 1.8
Color: white
Solubility: low-molecular-weight ketone or ester
Mooney viscosity: ML 1+10 @ 121℃ 45
5. CG-A25P
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Contents: binary mixture of vinylidene bluoride and hexafluoropropylene, vulcanizing agent included.
Characteristics: very good hot tear resistance and high curing speed.
Processing mode: injection molding and extrusion molding.
Vulcanization system: bisphenol
Fluorine content: 66 percent
Specific gravity: 1.8
Color: white
Solubility: low-molecular-weight ketone or ester
Mooney viscosity: ML 1+10 @ 121℃ 30
6. CG-E60C
Contents: binary mixture of vinylidene fluoride and hexafluoropropylene.
Moderate Mooney
Processing mode: mold pressing, flow mold pressing.
Characteristics: unique technique for vulcanizing agent mixing; good mold unload property and scorch safety; applicable to O rings or washers.
Fluorine content: 66 percent
Specific gravity: 1.82
Color: permalba
Solubility: ketone or ester.
Mooney viscosity: 46（ML1+10@121℃）
7. CG-F2462P
Applications: for solvent resistant sealing materials or for fuel oil, and extruded fuel hose; general fluorine mixed glue.
Packaging: PE bags (5 kg net), stored in cardboard boxes (25 kg net).
Ingredients: ternary mixture of vinylidene fluoride, tetrafluoroethylene and hexafluoropropylene.
Moderate Mooney.
Processing mode: mold pressing, extrusion molding.
Characteristics: unique techniques for vulcanizing agent mixing; good mold unload property and scorch safety.